Siddh Chemiplast PC compound is a mixture of PC resin, specific reinforcements and additives in different formulas to meet characteristics of each end products. It is highly recommended for end products which require great abrasion resistance, high durability and low shrinkage. Siddh Chemiplast provides customers with a series of PC compounds, including: PC glass fiber compound (PC-GF) PC coloured compound PC/PBT blend PC/PET blend
PC white compound is a combination of PC resin, pigment and specific additives.
| Criteria | Measurement Methods | Unit | ECP PC WH1012 |
|---|---|---|---|
| Colour | White | ||
| Melt Flow Index (MFI) (300°C/1.2kg) | ISO 1133 | g/10 min | 13 |
| Density | ISO 1183 | g/cm³ | 1.18 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 63 |
| Elongation at Break (a) | ISO 527 | % | >100 |
| Flexural Modulus | ISO 178 | MPa | 2010 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 10.5 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 123 |
| Flammability | UL 94 | V2 |
PC-GF compound is made of PC resin mixed with glass fiber. It helps to improve stiffness, thermal properties and impact strength of end products.
| Criteria | Measurement Methods | Unit | ECP PC WH10GF | ECP PC WH30GF |
|---|---|---|---|---|
| Colour | Natural | Natural | ||
| Melt Flow Index (MFI) (300°C/1.2kg) | ISO 1133 | g/10 min | 10 | 15 |
| Density | ISO 1183 | g/cm³ | 1.25 | 1.34 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 78 | 95 |
| Elongation at Break (a) | ISO 527 | % | >5 | >5 |
| Flexural Modulus | ISO 178 | MPa | 4521 | 6330 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 10 | 25 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 132 | 138 |
| Flammability (1.6 mm) | UL 94 | V2 | V2 |
PC-FR compound is made of PC resin mixed with halogen flame retardant. Depending on customer’s requirements, Siddh Chemiplast provides a series of compounds with different levels of flame retardancy according to UL94 standard: 5VA, 5VB, V0, V1, V2.
| Criteria | Measurement Methods | Unit | ECP PC WH 101 | ECP PC WH 102 V0 |
|---|---|---|---|---|
| Colour | White | White | ||
| Melt Flow Index (MFI) (300°C/1.2kg) | ISO 1133 | g/10 min | 34 | 34 |
| Density | ISO 1183 | g/cm³ | 1.22 | 1.21 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 60 | 61 |
| Elongation at Break (a) | ISO 527 | % | >5 | >5 |
| Flexural Modulus | ISO 178 | MPa | 2265 | 2270 |
| Izod Impact Strength (b) | ISO 180 | J/m | 103 | 105 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 118 | 120 |
| Flammability | UL 94 | 5VA | V0 |
PC/PBT compound is a blend of PC and PBT. It has great advantages of both PC and PBT, including high mechanical strength, good chemical resistance, and high-pressure resistance. PC/PET compound is a blend of PC and PET. It inherits great properties of both PC and PET, resulting in end products with excellent hardness, high impact resistance, glossiness, flexibility (even in low temperature environment), chemical resistance and electrical insulation.
| Criteria | Measurement Methods | Unit | ESC PC-PBT R 001BK | ESC PC-PET R 002 BK |
|---|---|---|---|---|
| Colour | Black | Black | ||
| Melt Flow Index (MFI) (260°C / 2.16 kg) | ISO 1133 | g/10 min | 17 | 9 |
| Density | ISO 1183 | g/cm³ | 1.24 | 1.19 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 53 | 55 |
| Elongation at Break (a) | ISO 527 | % | 5-10 | 5-10 |
| Flexural Modulus | ISO 178 | MPa | 2270 | 1734 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 43 | 27 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 87 | 122 |
PC/ABS-GF compound is a blend of PC and ABS resin and reinforced with glass fiber. It helps to increase the stiffness, thermal ability and impact strength of end products.
| Criteria | Measurement Method | Unit | ESC PC-ABS GR7001 |
|---|---|---|---|
| Colour | — | — | Grey |
| Melt Flow Index (MFI) (260°C / 2.16 kg) | ISO 1133 | g/10 min | 9 |
| Density | ISO 1183 | g/cm³ | 1.1 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 57 |
| Elongation at Break (a) | ISO 527 | % | 5–10 |
| Flexural Modulus | ISO 178 | MPa | 2204 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 25 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 106 |
PC/ABS-GF compound is a blend of PC and ABS resin and reinforced with glass fiber. It helps to increase the stiffness, thermal ability and impact strength of end products.
| Criteria | Measurement Method | Unit | ECP PC-ABS BK015GF | ECP PC-ABS BK025GF |
|---|---|---|---|---|
| Colour | — | — | Black | Black |
| Glass fiber content | TGA | % | 15 | 25 |
| Density | ISO 1183 | g/cm³ | 1.28 | 1.13 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 85 | 92 |
| Elongation at Break (a) | ISO 527 | % | >5 | >5 |
| Flexural Modulus | ISO 178 | MPa | 4231 | 6452 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 75 | 68 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 115 | 126 |