Siddh Chemiplast PA66, PA6 compound is made of PA resin and reinforced with glass beads or glass fibers. It has a high level of mechanical precision and abrasion resistance Siddh Chemiplast provides customers with a series of PC compounds, including: PA6, PA66 glass fiber (PA6, PA66-GF) PA6, PA66 flame retardant (PA6, PA66-FR) Blend PA6, PA66
PA6, PA66-GF compound is created by PA6, PA66 and glass fibers as the reinforcement. This material provides end products with stiffness improvement, shrinkage reduction, impact strength and thermal durability enhancement.
| Criteria | Measurement Method | Unit | ECP PA6 WH115GF | ECP PA6 N30GF | ECP PA66 N15GF | ECP PA66 N30GF | ECP PA66 N35GF |
|---|---|---|---|---|---|---|---|
| Colour | — | — | White | Natural | Natural | Natural | Natural |
| Glass fiber content | TGA | % | 15 | 30 | 15 | 30 | 35% |
| Density | ISO 1183 | g/cm³ | 1.21 | 1.35 | 1.24 | 1.36 | 1.45 g/cm³ |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 70 | 125–130 | 124 | 164 | 184 MPa |
| Elongation at Break (a) | ISO 527 | % | >5 | 3-5 | >5 | 3-5 | 3-5% |
| Flexural Modulus | ISO 178 | MPa | 3426 | 5218 | 5751 | 6951 | 6537 MPa |
| Izod Impact Strength (b) | ISO 180 | J/m | 52 | 70 | 40 | 41 | 50 J/m |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 165 | 190 | 225 | 232 | 240 °C |
| Flammability | UL 94 | — | HB | HB | HB | HB | HB |
PA6, PA66-FR compound is made of PA6, PA66 resin and flame retardants (halogen or non-halogen) in different levels according to UL94 standard (V0, V1, V2).
| Criteria | Measurement Method | Unit | ESC PA6 N10 GV0 | ESC PA6 NV0NH |
|---|---|---|---|---|
| Colour | — | — | Natural | Natural |
| Glass fiber content | TGA | % | 10 | — |
| Density | ISO 1183 | g/cm³ | 1.4 | 1.19 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 76 | 63 |
| Elongation at Break (a) | ISO 527 | % | 3–5 | >10 |
| Flexural Modulus | ISO 178 | MPa | 3890 | 3710 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 10 | 6 |
| Deflection Temperature under Load at 0.45 MPa (b) | ISO 75 | °C | 180 | 180 |
| Flammability | UL 94 | — | V0 | V0 |
PA6, PA66 blend compound is a combination of PA6, PA66 resin and elastomer. Thanks to its great mechanical properties and thermal ability, blend PA6, PA66 significantly improves end products flexibility and impact strength.
| Criteria | Measurement Method | Unit | ECP PA66 BK001 |
|---|---|---|---|
| Colour | — | — | Black |
| Density | ISO 1183 | g/cm³ | 1.15 |
| Tensile Strength at Yield (a) | ISO 527 | MPa | 50 |
| Elongation at Break (a) | ISO 527 | % | >100 |
| Flexural Modulus | ISO 178 | MPa | 1282 |
| Izod Impact Strength (b) | ISO 180 | kJ/m² | 36 |
| Deflection Temperature under Load at 1.8 MPa (b) | ISO 75 | °C | 55 |
| Flammability | UL 94 | — | HB |